| Type: | Stainless Steel Strips |
|---|---|
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
| Grade: | 300 Series |
| Certification: | ISO, RoHS, IBR, AISI, ASTM, GB, EN, DIN, JIS |
| Shape: | Round |
| Technique: | Cold Rolled |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier | Tianjin Standard Steel Co., Ltd | ||||
| Commodity | Stainless Steel Coil/Stainless Steel Roll | |||
| Material | 301 | |||
| Standard | GB | JIS | ASTM/ASME | DIN |
| 12Cr17Ni7 | SUS301 | 301 | 1.4319 | |
| Chemical Composition | C | Mn | P | S |
| ≤ 0.15 | ≤ 2 | ≤ 0.045 | ≤ 0.03 | |
| Si | Cr | N | Ni | |
| ≤ 1 | 16~18 | ≤ 0.1 | 6~8 | |
| Thickness | 0.3mm--6mm(cold rolled) 3mm--16mm(hot rolled) | |||
| Width | 1000mm--2200mm | |||
| Length | 1000mm-6000mm, as customers' request | |||
| Surface | BA/2B/NO. 1/NO. 3/NO. 4/8K/HL/2D/1D | |||
| manufacture | Hot Rolled/Cold Rolled | |||
| Packing | Packed in bundles with standard export sea-worthy package | |||
| Delivery Time | Within 15 working days, according to customers' quantities | |||
| Quality | High Quality. SGS inspection is accepted if needed | |||
| Place of Origin | Tianjin | |||
| Productivity | 500 MT/Month | |||
| Payment | T/T, L/C | |||
| MOQ | 1 MT | |||
| Application | Foodstuff, Gas, metallurgy, biology, electron, chemical etc. | |||
| Note | We can also do other materials | |||
| Chemical composition of stainless steel | ||||||||||||
| standard name | chemical composition | |||||||||||
| ASTM | EN | GB | JIS | KS | C(carbon) | Si(silicon) | Mn(manganese) | Cr(chromium) | Ni(nickel) | S(sulfur) | P(phosphorus) | others |
| 201 | 1.4372 | 1Cr17Mn6Ni5N | SUS201 | STS201 | ≤0.15 | ≤1.0 | 5.5~7.5 | 16.0~18.0 | 3.5~5.5 | ≤0.030 | ≤0.060 | N:≤0.025 |
| 202 | 1.4373 | 1Cr18Mn8Ni5N | SUS202 | STS202 | ≤0.15 | ≤1.0 | 7.5~10.0 | 17.0~19.0 | 4.0~6.0 | ≤0.030 | ≤0.060 | N:≤0.025 |
| 301 | 1.4319 | 1Cr17Ni7 | SUS301 | STS301 | ≤0.15 | ≤1.0 | ≤1.0 | 17.0~18.0 | 6.0~8.0 | ≤0.200 | ≤0.020 | - |
| 304 | 1.4301 | 0Cr18Ni9 | SUS304 | STS304 | ≤0.08 | ≤1.0 | ≤2.0 | 17.0~19.0 | 8.0~11.0 | ≤0.030 | ≤0.035 | - |
| 321 | 1.4541 | 1Cr18Ni9Ti | SUS321 | STS321 | ≤0.12 | ≤1.0 | ≤2.0 | 17.0~19.0 | 8.0~11.0 | ≤0.030 | ≤0.035 | Ti:5C~7.0 |
| 304L | 1.4306 | 00Cr19Ni10 | SUS304L | STS304L | ≤0.03 | ≤1.0 | ≤2.0 | 18.0~20.0 | 8.0~12.0 | ≤0.030 | ≤0.035 | - |
| 309S | 1.4833 | 0Cr23Ni13 | SUS309S | STS309S | ≤0.08 | ≤1.0 | ≤2.0 | 22.0~24.0 | 12.0~15.0 | ≤0.030 | ≤0.035 | - |
| 310S | 1.4845 | 0Cr25Ni20 | SUS310S | STS310S | ≤0.08 | ≤1.0 | ≤2.0 | 24.0~26.0 | 19.0~22.0 | ≤0.030 | ≤0.035 | - |
| 316 | 1.4401 | 0Cr17Ni12Mo2 | SUS316 | STS316 | ≤0.08 | ≤1.0 | ≤2.0 | 16.0~18.0 | 10.0~14.0 | ≤0.030 | ≤0.035 | Mo:2.0~3.0 |
| 316L | 1.4404 | 00Cr17Ni14Mo2 | SUS316L | STS316L | ≤0.03 | ≤1.0 | ≤2.0 | 16.0~18.0 | 12.0~15.0 | ≤0.030 | ≤0.035 | Mo:2.0~3.0 |
| Finish | Description |
| 2D | A matt non-refective finish produced by cold rolling followed by annealing and descaling. The dull finish may result from the pickling operation or rolling on dull rolls |
| 2B | A bright, moderately reflective cold rolled with the annealed and descaled coil receiving a final light pass through polished rolls. This is the general purpose cold rolled finish that can be used as is, or as a preliminary step to polishing. 2B is the most commonly used surface finish |
| BA | Bright annealed is offered by many stainless steel producers, and is referred to as BA or No. 2BA. A bright annealed finish approaches a mirror-like appearence. It is produced by cold rolling, then annealing in a controlled atmosphere furnace. The final appearence is developed by a single light skin pass through a cold mill over highly polished rolls, but is also dependent on additional millwork, such as grinding the surface at an intermediate gauge. A bright annealed finish is often specified for architectural applications and for other uses where a reflective surface is desired on the as fabricated part. Some "milkiness" in the finish makes a BA finish not as reflective as No. 8. Typical uses include appliance trim, architectural components, cookware, food processing equipment |
| No.4 | No.4 finish is a general purpose polished finish widely used for restaurant equipment, shop fronts and dairy equipment. Following initial grinding with coarse abrasives, final finishing generally is done with abrasives having a particle size of approximately 120 to 150 mesh |
| No.8 | No. 8* finish, the most relective finish that is commonly produced on sheet, is obtained by polishing with successively finer abrasives and buffing extensively with very fine buffing rouges. The surface is essentially free of grit lines from preliminary grinding operations. No. 8 finish is most widely used for architectural parts, small mirrors and reflectors and for press plates |
| * Not a standard mill finish, but commonly available in some sheet sizes and included to show the range of finishes available |
|
| GRADE | DESIGNATION | Mechanical properties | ||||
| EN | AISI/ ASTM | Y.S (MPa) min | T.S (MPa) | Elongation (%)min | HB (Max) | |
| AUSTENITIC | 1.4372 | 201 | 330 | 750 to 950 | 40 | 241 |
| 1.4373 | 202 | 320 | 600 to 880 | 35 | 241 | |
| 1.4310 | 301 | 250 | 600 to 950 | 40 | 217 | |
| 1.4305 | 303 | 190 | 500 to 700 | 35 | ||
| 1.4301 | 304 | 210 | 520 to 720 | 45 | 149 | |
| 1.4306 | 304L | 200 | 500 to 700 | 45 | 143 | |
| 1.4303 | 305 | 220 | 500 to 650 | 45 | 183 | |
| 1.4833 | 309S | 210 | 500 to 700 | 33 | 192 | |
| 1.4845 | 310S | 210 | 500 to 700 | 33 | 192 | |
| 1.4841 | 314 | 230 | 550 to 750 | 28 | 223 | |
| 1.4401 | 316 | 220 | 530 to 730 | 40 | 149 | |
| 1.4406 | 316L | 220 | 520 to 670 | 45 | 146 | |
| 1.4571 | 316TI | 220 | 520 to 670 | 40 | 217 | |
| 1.4438 | 317L | 220 | 520 to 720 | 40 | 217 | |
| 1.4541 | 321 | 200 | 500 to 700 | 40 | 160 | |
| 1.4550 | 347 | 200 | 500 to 700 | 40 | 160 | |
| 1.4539 | 904L | 220 | 520 to 720 | 35 | ||